Crucible Liners for e-Guns™ and Other Electron Beam Evaporation Sources
Crucible liners are used with electron beam evaporation sources in applications throughout the coating industry. Crucible liners are widely accepted as part of the coating process, and are considered to be an integral component for coating success. Liners provide many advantages, for example:
- Higher yield
- Reduced maintenance
- Thermal isolation
- Reduced thermal gradient
- Higher evaporation rates
- Reduced contamination
- Improved performance
- Thermal stability
- Lower power requirements
- Reduced crucible damage
Our crucible liners are compatible
with many manufacturer's evaporation sources. Please review the ordering information for more details.
Benefits
Crucible liners provide thermal isolation between the evaporant material and the water-cooled crucible. Therefore, the evaporation process requires less power, and you will achieve:
- higher evaporation rates at the same power level, or
- the same evaporation rate at a lower power level.
Crucible liners reduce the thermal gradient across the evaporant material. This increases the thermal stability within the melt, thereby increasing heating efficiency and reducing particle ejection and oscillations within the molten material.
Using separate liners for each evaporant material can reduce contamination and provide extra protection against crucible damage.
Liner Materials
Crucible liners are available in various materials. Carbon graphite and glassy coated carbon graphite are two of the more common materials used. They are popular due to their low cost and favorable thermal properties.
Carbon graphite is a fine grain, high density polycrystalline material with interconnecting porosity. It can be purified to 5 ppm or less.
Glassy coated carbon graphite liners are made from the same high grade carbon as above, then baked in a coated graphite process above 1,400°C to eliminate any porosity in the carbon.
FABMATE® crucible liners are an alternative to the glassy coated graphite. FABMATE receives an amorphous carbon treatment to provide a hard, abrasion resistant, nonporous surface.
Other crucible liner materials include:
- Alumina
- Boron Nitride
- Copper
- Molybdenum
- Tantalum
- Tungsten
Liners made from these more exotic materials are more expensive and typically limited to special applications.
Ordering information
Handling
Maximizing the life of a crucible liner requires careful attention to handling and storage. Never handle liners with bare hands. Liners should be handled with gloves, tongs or finger cots. Graphite, coated graphite and FABMATE® liners should not be cleaned with chemicals or solvents of any kind. Used liners should be stored in a dry, oxygen-free environment.
Better Utilization of Liners
Proper technique is important, otherwise crucible liners will break due to thermal shock. Breakage, however, can be minimized. In addition, some materials become highly reactive when molten and may alloy to the liner.
The most common cause of crucible liner breakage is thermal shock. Overfilling a liner can cause the evaporant material to "spill over" the liner onto the water-cooled crucible surface. This causes an increased thermal stress across the liner and in most cases will cause it to crack or shatter.
Liners should be filled with evaporant material at a level of no less than 25% volume and no more than 80% volume. Aluminum has a tendency to "wet" most liner materials and requires a reduced maximum charge level of 70%. Aluminum becomes highly reactive when molten and as a result will eventually react with any material.